商品特点:该产品具有内外表面高清洁、超光亮、组织均匀致密、尺寸精度高、换热效率高、易焊接、耐腐蚀、使用成型性好等优点
执行标准:GB/T17791
下表列出外径、壁厚等参数
规格 |
状态 |
平均外径 |
平均壁厚 |
最大运行压力 |
爆破压力 |
(mm) |
(mm) |
(Mpa) |
(Mpa) |
||
φ15.88*0.41 |
M |
15.88 |
0.4 |
2.57 |
11.83 |
φ15.88*0.5 |
M |
15.88 |
0.48 |
3.1 |
14.25 |
φ15.88*0.7 |
M |
15.88 |
0.68 |
4.43 |
20.4 |
φ15.88*0.8 |
M |
15.88 |
0.77 |
5.04 |
23.2 |
Φ15.88*0.9 |
M |
15.88 |
0.87 |
5.73 |
26.36 |
φ15.88*1.0 |
M |
15.88 |
0.97 |
6.42 |
29.54 |
φ16*0.8 |
M |
16 |
0.77 |
5.01 |
23.02 |
φ16*1.0 |
M |
16 |
0.97 |
6.37 |
29.31 |
φ16*1.5 |
M |
16 |
1.45 |
9.77 |
44.95 |
φ19*0.7 |
M |
19 |
0.68 |
3.68 |
16.95 |
φ19*0.75 |
M |
19 |
0.72 |
3.91 |
17.98 |
φ19*0.8 |
M |
19 |
0.77 |
4.19 |
19.27 |
φ19*0.9 |
M |
19 |
0.87 |
4.75 |
21.86 |
φ19*1.0 |
M |
19 |
0.96 |
5.27 |
24.22 |
φ19.05*0.7 |
M |
19.05 |
0.68 |
3.67 |
16.90 |
φ19.05*0.8 |
M |
19.05 |
0.77 |
4.18 |
19.21 |
φ19.05*0.9 |
M |
19.05 |
0.87 |
4.74 |
21.80 |
φ19.05*1.0 |
M |
19.05 |
0.97 |
5.31 |
24.42 |
参数说明:
1.表中各个规格的最大运行压力根据理论公式计算得出,部分规格做过验证试验,但由于铜管本身存在尺寸
差异以及细微缺陷,因此上表压力数值仅供参考,新机型或新运行环境设计仍需实际验证作为依据
2.铜管经过弯制、扩口、胀管、攻丝等操作后机械性能和局部尺寸会发生变化,实际应用中需要考虑在内
连铸连轧:
连铸工艺----采用等压铸造与电磁改性新技术,稳定铸造液面,消除铸坯裂纹,细化铸坯晶粒,提高产品性能
轧管工艺----采用新辊型、新型芯棒头和轧辊连接新结构技术,通过提高轧制温度,使轧管晶粒更均匀,减少轧辊窜动,从而进一步提
高了轧管同心度
拉伸工艺----采用三联拉与防共振盘拉组合拉伸新技术,减轻管间擦伤,减弱管外表面纵向缺陷,减小壁厚偏差显著提高了铜管尺寸精
度和同心度
涡流探伤:利用电磁感应原理,检测导电构件表面和近表面缺陷的一种探伤方法。通过涡流探伤的铜管,在有缺陷和隐患的地方喷涂
上40公分左右长度的黑墨,在安装使用一定将其喷墨部分去掉从而保证使用质量
清洗脱油:使铜管内壁达到R410A冷煤的使用条件
特别说明:
在安装过程中经试压、铜管出现渗漏、开裂、砂眼等质量问题,一个坏点(喷墨伤点除外)按500元一次性赔付,同时金牛公司不承担连带责任